检测范围
- 奥氏体不锈钢循环极化测试
- 双相不锈钢循环极化测试
- 马氏体不锈钢循环极化测试
- 沉淀硬化不锈钢循环极化测试
- 铝镁合金循环极化测试
- 钛合金循环极化测试
- 镍基合金循环极化测试
- 铜合金循环极化测试
- 钴铬合金循环极化测试
- 碳钢材料循环极化测试
- 合金钢材料循环极化测试
- 镀锌钢材循环极化测试
- 渗氮处理钢材循环极化测试
- 阳极氧化铝合金循环极化测试
- 化学转化膜涂层循环极化测试
- 热喷涂涂层循环极化测试
- 堆焊层材料循环极化测试
- 管道焊缝区域循环极化测试
- 换热器管材循环极化测试
- 海洋工程用钢循环极化测试
- 医疗植入金属循环极化测试
- 核电用锆合金循环极化测试
检测标准（部分）
- YY/T 0695-2008 小型植入器械腐蚀敏感性的循环动电位极化标准测试方法
- ASTM G100-89(2021) Standard Test Method for Conducting Cyclic Galvanostaircase Polarization
- ASTM F2129-25 Standard Test Method for Conducting Cyclic Potentiodynamic Polarization Measurements to Determine the Corrosion Susceptibility of Small Implant Devices
- ASTM G100-89(2015) Standard Test Method for Conducting Cyclic Galvanostaircase Polarization
- ASTM G61-86(2024) Standard Test Method for Conducting Cyclic Potentiodynamic Polarization Measurements for Localized Corrosion Susceptibility of Iron-, Nickel-, or Cobalt-Based Alloys
- KS D 2614 반복된 정전위와 정전류 인가를 통한 도장된 강재 현가 부품의 가속내식성 평가방법
- ASTM G100-89(2010)e1 Standard Test Method for Conducting Cyclic Galvanostaircase Polarization
- GB/T 44653-2024(英文版) 六氟化硫（SF6）气体的现场循环再利用导则
- KS D 2614-2023 반복된 정전위와 정전류 인가를 통한 도장된 강재 현가 부품의 가속내식성 평가방법
- ASTM G100-89(2004) Standard Test Method for Conducting Cyclic Galvanostaircase Polarization
- T/CZRX 0090-2024 高容量钠离子电池磷化物负极材料循环稳定性试验方法
- KS D 0280-2020 철, 니켈, 코발트 합금의 국부적인 부식 민감도에 대한 순환 동전위 분극 시험 방법
- KS D 0280(2025 Confirm)(2025) 철, 니켈, 코발트 합금의 국부적인 부식 민감도에 대한 순환 동전위 분극 시험 방법
- KS D 0280-2020(2025) 철, 니켈, 코발트 합금의 국부적인 부식 민감도에 대한 순환 동전위 분극 시험 방법
- ASTM G100-89(1999) Standard Test Method for Conducting Cyclic Galvanostaircase Polarization
- ASTM F2129-19 Standard Test Method for Conducting Cyclic Potentiodynamic Polarization Measurements to Determine the Corrosion Susceptibility of Small Implant Devices
- ASTM F2129-19a Standard Test Method for Conducting Cyclic Potentiodynamic Polarization Measurements to Determine the Corrosion Susceptibility of Small Implant Devices
- ASTM F2129-24 Standard Test Method for Conducting Cyclic Potentiodynamic Polarization Measurements to Determine the Corrosion Susceptibility of Small Implant Devices
- ASTM F2129-17b Standard Test Method for Conducting Cyclic Potentiodynamic Polarization Measurements to Determine the Corrosion Susceptibility of Small Implant Devices
- ASTM F2129-17 Standard Test Method for Conducting Cyclic Potentiodynamic Polarization Measurements to Determine the Corrosion Susceptibility of Small Implant Devices
常见问题
循环极化检测需要多长时间？通常7-15个工作日
常规样品的循环极化检测通常需要7-15个工作日完成，具体周期视样品数量及测试介质条件而定。
循环极化检测费用大概多少？根据检测项目数量确定
循环极化检测费用根据检测项目数量确定，若需额外测定不同温度或不同氯离子浓度下的极化曲线，费用会相应调整。
循环极化检测对样品有什么要求？
样品需加工成特定尺寸的工作电极，暴露测试面积通常为1平方厘米，表面需依次使用砂纸打磨抛光至规定粗糙度并经超声清洗除油。
循环极化测试中正向扫描和反向扫描有什么区别？
正向扫描用于引发点蚀并测定点蚀电位，反向扫描用于观察再钝化行为并测定保护电位，两者形成的滞后环是判断局部腐蚀敏感性的关键。
循环极化检测仪器
- 电化学工作站
- 恒电位仪
- 恒温水浴槽
- 标准三电极电解池
- 饱和甘汞参比电极
- 铂片辅助电极
- 盐桥装置
- 高纯氮气脱气装置
- 金相试样抛光机
- 表面粗糙度仪
检测信息
循环极化是一种电化学动电位扫描测试技术，用于评估金属材料在特定腐蚀介质中的局部腐蚀敏感性，主要应用于不锈钢、铝合金等耐蚀性能分析领域。
检测目的在于通过测定材料的点蚀电位和再钝化电位，评价其耐点蚀和缝隙腐蚀的能力，涉及动电位扫描和电化学阻抗测试等技术手段。
检测流程包括样品制备、电解液脱气、开路电位稳定测试、正向极化扫描至预设电流阈值以及反向扫描回起始电位，核心参数包括滞后环面积和保护电位差值。
总结
循环极化是评估金属材料局部腐蚀敏感性的电化学检测，覆盖点蚀电位、保护电位及再钝化行为等核心参数测定。北京中科光析科学技术研究所检测中心可提供该项目的测试服务。常规检测周期为7-15个工作日。